Silica Brick for Hot Blast Furnace
Product Description
Item | Specification |
SiO2 % ≥ | 95 |
Al2O3 % ≤ | 1.0 |
Fe2O3 % ≤ | 1.3 |
Cold crushing strength Mpa ≥ | 45 |
Apparent porosity % ≤ | 22 |
Creep reate 0.2MPa 1500℃ 50h % ≤ | 0.8 |
Apparent density g/cm3 ≤ | 2.32 |
Thermal expansion 1000℃ % ≤ | 1.25 |
Residual quartz % ≤ | 1.0 |
Refractoriness under load T0.6 ℃ ≥ | 1650 |
Silica bricks are made from silica≥ 96%, adding mineralizers and binders, and going through processes such as mixing, molding, drying, and sintering.
characteristic:
Silica brick is an acid refractory material with strong resistance to acid or erosion.
The high soft temperature is an excellent characteristic of silica brick, generally 1640~1680℃.
Usage:
Silica bricks are mainly used to build the carbonization chamber, combustion chamber and partition walls of coke ovens (about 73% of the refractory materials used in a coke oven are silica bricks), the kiln roof, pool walls, and high temperature load-bearing parts of hot blast stoves. , carbon roasting furnace and other thermal kilns