High temperature refractory fire brick for Steel Industry
Product Description
High Alumina Brick & Low-creep High Alumina Brick for Hot Blast Furnace
Items | High Alumina Brick | Low-creep High Alumina Brick | |||||
RL-65 | RL-55 | RL-48 | DRL-145 | DRL-140 | DRL-135 | DRL-130 | |
Al2O3 % ≥ | 65 | 55 | 48 | 65 | 65 | 65 | 60 |
B.D g/cm³ ≥ | — | — | — | 2.6 | 2.5 | 2.45 | 2.4 |
A.P % ≤ | 22（24） | 22（24） | 22（24） | 21 | 22 | 22 | 22 |
C.C.S Mpa ≥ | 50 | 45 | 40 | 60 | 55 | 55 | 55 |
℃ Refractoriness ≥ | 1780 | 1760 | 1740 | 1790 | 1790 | 1790 | 1770 |
0.2Mpa R.U.L ℃ T0.6 ≥ | 1500 | 1470 | 1420 | 1600 | 1580 | 1550 | 1520 |
P.L.C % | 1500℃×2h +0.1~-0.4 | 1500℃×2h +0.1~-0.4 | 1450℃×2h +0.1~-0.4 | 1550℃×2h +0.1~0.4 | 1450℃×2h +0.1~0.2 | 1450℃×2h +0.1~0.4 | 1450℃×2h +0.1~0.4 |
Creep rate % ≤(0.2Mpa×50h) | — | — | — | 1450℃ 0.8 | 1400℃ 0.8 | 1350℃ 0.8 | 1300℃ 0.8 |
T.S.R(1100℃ water-cycle)≥ | 6 | furnish data measured | |||||
Aluminum silicate refractory bricks with aluminum oxide (Al2O3) content higher than 48%.
High alumina refractory brick is formed and calcined from bauxite or other raw materials with high alumina content. High thermal stability, refractoriness above 1770℃. It has good slag resistance and is used for the lining of steel-making electric furnaces, glass melting furnaces, cement rotary furnaces, etc.
Features:
High alumina brick has the advantages of small high temperature creep, strong corrosion resistance, good thermal shock stability, etc. It is suitable for large and medium-sized hot blast stoves.
Application:
High alumina bricks are mainly used for masonry blast furnace, hot blast stove, electric furnace roof, blast furnace, rotary kiln lining. In addition, high alumina bricks are also widely used as open hearth regenerative checker bricks, plugs for pouring systems, nozzle bricks, etc.
Kaiyuan high alumina bricks were exported to Japan, South Korea, UK, Germany and many other countries.